Experimental and theoretical approaches on thermal and structural properties of Zn doped BSCCO glass ceramics


Creative Commons License

Koralay H. , Hicyilmaz O., Cavdar Ş. , Ozturk O., Tasci A. T.

MATERIALS SCIENCE-POLAND, vol.34, no.1, pp.25-32, 2016 (Journal Indexed in SCI) identifier identifier

  • Publication Type: Article / Article
  • Volume: 34 Issue: 1
  • Publication Date: 2016
  • Doi Number: 10.1515/msp-2016-0027
  • Title of Journal : MATERIALS SCIENCE-POLAND
  • Page Numbers: pp.25-32

Abstract

Thermal properties of Cu-Zn partially substituted Bi1.8Sr2Ca2Cu3.2-xZnxO10+delta (x = 0, 0.1 and 0.5) glass-ceramic systems have been investigated with the help of a differential thermal analyzer (DTA) by using Johnson-Mehl-Avrami-Kolmogorov (JMAK) approximation. Non-isothermal crystallization kinetics of the samples has been tested. The calculated values of activation energy of crystallization (E) and Avrami parameter (n) ranged between 306.1 and 338.3 kJ.mol(-1) and 1.29 and 3.59, respectively. Crystallization kinetics was compared following the partial substitution, before and after Zn doping of the sample. In addition, by using a scanning electron microscope (SEM) and X-ray powder diffractometer (XRD), structural properties of Zn doped BSCCO glass-ceramic samples were determined. Surface morphology of the samples was studied by SEM measurements. Lattice parameters and volume of the samples were calculated from the XRD measurements.