Bonding Strength of Some Adhesives in Heat-Treated Hornbeam (Carpinus betulus L.) Wood Used for Interior and Exterior Decoration
BIORESOURCES, cilt.11, sa.3, ss.7686-7696, 2016 (SCI-Expanded, Scopus)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 11 Sayı: 3
- Basım Tarihi: 2016
- Doi Numarası: 10.15376/biores.11.3.7686-7696
- Dergi Adı: BIORESOURCES
- Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
- Sayfa Sayıları: ss.7686-7696
- Anahtar Kelimeler: Heat treatment, Glue, Bonding strength, Hornbeam (Carpinus betulus L.), THERMALLY MODIFIED WOOD, MECHANICAL-PROPERTIES, MASS-LOSS, TEMPERATURE, SPRUCE, PERFORMANCE, RESONANCE, PINE
- Açık Arşiv Koleksiyonu: AVESİS Açık Erişim Koleksiyonu
- Gazi Üniversitesi Adresli: Evet
Özet
Heat-treated wood has an ever-expanding market for exterior and interior applications. The objective of this study was to determine the effect of a heat treatment on the bonding strength of hornbeam (Carpinus betulus L.) wood that was bonded with melamine formaldehyde (MF), polyurethane (PUR), and polyvinyl acetate (PVAc-D4) adhesives. Hornbeam lamellas were heat treated at 150 degrees C, 175 degrees C, 200 degrees C, and 225 degrees C for 3 h and then bonded. The bonding strength of the specimens was determined. In addition, the density, weight loss, and pH value of the heat-treated wood were investigated. The results showed that the bonding strengths of the heat-treated wood specimens decreased with the temperature of the heat treatment. The bonding strength of the PUR adhesive was higher than the MF and the PVAc-D4.