Recrystallization kinetic of Fe-5.23%V and Fe-15%V alloys Fe-%5,23V ve Fe-%15V alaşimlarinin yeniden kristalleşme kinetiǧi


BOSTAN B. , ÖZDEMİR A. T.

Journal of the Faculty of Engineering and Architecture of Gazi University, vol.18, no.1, pp.101-108, 2003 (Journal Indexed in SCI Expanded) identifier

  • Publication Type: Article / Article
  • Volume: 18 Issue: 1
  • Publication Date: 2003
  • Title of Journal : Journal of the Faculty of Engineering and Architecture of Gazi University
  • Page Numbers: pp.101-108

Abstract

In this work, binary alloys of Fe-5,23%V and Fe-15%V were first cold rolled by 50% and then annealed in an oxygen-free set-up at 560, 570, 580 and 590°C, respectively. It was found that the rate of recrystallization obeyed an Avrami type equation in which time exponent was temperature independent. It was concluded that increase in vanadium content accelerated, the rate of transformation where on the contrary did not influenced the general trend of the hardness variation.