Processing of Fireproof and High Temperature Durable Particleboard from Rice Husk


GÜRÜ M., Karabulut A. F., Aydin M. Y., Bilici I.

HIGH TEMPERATURE MATERIALS AND PROCESSES, vol.34, no.6, pp.599-604, 2015 (SCI-Expanded) identifier identifier

Abstract

The aim of this study is the recovery of rice husk waste by researching usability in industry as an alternative to wood. In this study urea formaldehyde resin was used mainly as binding agent for wood-panel used in industry. For the preparation of composite material, ground powder rice husks were mixed with urea formaldehyde resin used in different proportions (65/50, 75/50, 80/50, 85/50, 95/50 by mass of filler/binder). Each particleboard produced in 393.15 K and 9.8 MPa pressure was tested by means of three point bending strength, shore hardness and limited oxygen index (LOI) tests. Particleboard made with 75/50 paddy husk/urea formaldehyde composition material formed of 11.40 MPa specimens showed the highest strength. Limited oxygen index value increased by increasing the filler material usage. The highest LOI value was recorded as 40%. Besides, fire point of particleboards which have the best three point bending strength has been analyzed at environmental atmosphere and 493.15 K has been measured as fire point. The results of the tests showed that this material maybe used instead of wooden plate. The usage of agricultural wastes like these in processing of particleboard will give economically benefits and slow down waste products.