Effect of post-space treatments on the push-out bond strength and failure modes of glass fibre posts

DENİZ ARISU H., Kivanc B., Saglam B. C., Simsek E., Gorgul G.

AUSTRALIAN ENDODONTIC JOURNAL, cilt.39, sa.1, ss.19-24, 2013 (SCI-Expanded) identifier identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 39 Sayı: 1
  • Basım Tarihi: 2013
  • Doi Numarası: 10.1111/j.1747-4477.2010.00275.x
  • Dergi Adı: AUSTRALIAN ENDODONTIC JOURNAL
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.19-24
  • Anahtar Kelimeler: diode laser, endodontically treated tooth, fibre post, push-out test, SMEAR LAYER REMOVAL, ROOT-CANAL TREATMENT, DIODE-LASER, SODIUM-HYPOCHLORITE, DENTIN, MICROTENSILE, RETENTION, CEMENTS, WALLS, IRRADIATION
  • Gazi Üniversitesi Adresli: Evet

Özet

The aim of this study was to evaluate the effect of different post-space treatments on the push-out bond strength and failure modes of glass fibre posts. Forty mandibular premolar roots were cut and endodontically treated. Post spaces were prepared and roots were divided into four groups. In group 1 distilled water irrigation (control), in group 2 2.25% NaOCl irrigation, in group 3 2.25% NaOCl+17% EDTA irrigation were done and in group 4 diode laser was applied to the prepared post spaces. Scanning electron microscope (SEM) analysis was made for each group. Fibre posts were then luted with resin cement. Each root was prepared for push-out test. Data were statistically analysed with anova (P=0.05). After push-out test, the failure modes were observed but not statistically analysed. There were statistically significant differences between Group 3 and Group 2 in both regions (P<0.05), also in the middle region of Group 4 and Group 2 (P<0.05). Cervical root segments showed higher bond strengths than middle ones in all groups (P<0.05). The highest bond strength values were obtained from NaOCl/EDTA and the lowest bond strength values were obtained from NaOCl for both regions.