Resin cementation of zirconia ceramics with different bonding agents

Tanis M., Akay C., Karakış D.

BIOTECHNOLOGY & BIOTECHNOLOGICAL EQUIPMENT, cilt.29, sa.2, ss.363-367, 2015 (SCI-Expanded) identifier identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 29 Sayı: 2
  • Basım Tarihi: 2015
  • Doi Numarası: 10.1080/13102818.2014.996606
  • Dergi Adı: BIOTECHNOLOGY & BIOTECHNOLOGICAL EQUIPMENT
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.363-367
  • Anahtar Kelimeler: zirconia, resin cement, MDP monomer, primer agents, SURFACE CONDITIONING METHODS, LUTING AGENT, FLEXURAL STRENGTH, ADHESION, PRIMERS, PERFORMANCE, DURABILITY
  • Gazi Üniversitesi Adresli: Evet

Özet

The aim of this study was to evaluate the effects of sandblasting and different chemical bonding agents on shear bond strength of zirconia and conventional resin cement. In this study, 35 zirconia specimens were treated as follows: Group I: control; Group II: sandblasting; Group III: sandblasting + Monobond S; Group IV: sandblasting + Monobond Plus; Group V: sandblasting + Z-Prime Plus. The specimens in each group were bonded with conventional composite resin cement Variolink II. After cementation, specimens were stored in distilled water (at 37 degrees C) for 24 h and shear test was performed. The highest shear bond strength values were observed in Groups IV and V. The lowest shear bond strength values were observed in Group I. Using 10-methacryloyloxy-decyl dihydrogenphosphate monomer-containing priming agents, e.g. Monobond Plus and Z-PRIME Plus, combined with sandblasting can be an effective method for resin bonding of zirconia restorations.