Scattering analysis of 2DEG carrier extracted by QMSA in undoped Al0.25Ga0.75N/GaN heterostructures

Creative Commons License

LİŞESİVDİN S. B., ACAR S., Kasap M., Ozcelik S., Gokden S., Ozbay E.

SEMICONDUCTOR SCIENCE AND TECHNOLOGY, cilt.22, sa.5, ss.543-548, 2007 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 22 Sayı: 5
  • Basım Tarihi: 2007
  • Doi Numarası: 10.1088/0268-1242/22/5/015
  • Dergi Adı: SEMICONDUCTOR SCIENCE AND TECHNOLOGY
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.543-548
  • Gazi Üniversitesi Adresli: Evet

Özet

Hall effect measurements on undoped Al0.25Ga0.75N/GaN heterostructures grown by a metalorganic chemical vapour deposition (MOCVD) technique have been carried out as a function of temperature (20-350 K) and magnetic field (0-1.5 T). Magnetic field dependent Hall data were analysed using the quantitative mobility spectrum analysis (QMSA) technique. The mobility and density within the two-dimensional electron gas (2DEG) at the Al0.25Ga0.75N/GaN interface and within the underlying GaN layer were successfully separated by QMSA. Mobility analysis has been carried out using both the measured Hall data at a single field and the extracted data from QMSA. Analysis of the temperature-dependent mobility of 2DEG extracted from QMSA indicates that the interface roughness and alloy disorder scattering mechanisms are the dominant scattering mechanisms at low temperatures while at high temperatures only polar optical phonon scattering is the dominant mechanism. Al0.25Ga0.75N/GaN interface related parameters such as well width, deformation potential constant and correlation length were also accurately obtained from the fits of the simple analytical expressions of scattering mechanisms to the 2DEG mobility.