Performance evaluation of SILAR deposited Rb-Doped ZnO thin films for photodetector applications


Tekin S., ÜNVEROĞLU ABDİOĞLU B., Karaduman Er I., ACAR S.

Journal of Sol-Gel Science and Technology, cilt.111, sa.3, ss.891-908, 2024 (SCI-Expanded) identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 111 Sayı: 3
  • Basım Tarihi: 2024
  • Doi Numarası: 10.1007/s10971-024-06493-8
  • Dergi Adı: Journal of Sol-Gel Science and Technology
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, PASCAL, Aerospace Database, Applied Science & Technology Source, Biotechnology Research Abstracts, Chemical Abstracts Core, Chimica, Communication Abstracts, Compendex, Computer & Applied Sciences, Metadex, Civil Engineering Abstracts
  • Sayfa Sayıları: ss.891-908
  • Anahtar Kelimeler: Photodetector, Rare earth, Rubidium doped ZnO, Visible light
  • Gazi Üniversitesi Adresli: Evet

Özet

ZnO-based photodetectors (PDs) compose a remarkable optoelectronic device field due to their high optical transmittance, electrical conductivity, wide band gap, and high binding energy. This study examined the visible light photodetector performance of the pristine and Rubidium (Rb)-doped ZnO thin films. The influence of Rb doping amount (2, 4, and 6 wt% in solution) on the electrical, optical, and structural properties of the ZnO-based thin films produced by the Successive Ion Layer Adsorption and Reaction (SILAR) technique was analyzed. Structural analyses showed that all peaks correspond to hexagonal wurtzite structure with no other peak from Rb-based phases, suggesting the high quality of the crystalline pristine and Rb-doped ZnO thin films. The morphology of the thin films shows homogenous layers formed of nanoparticles where particle size was first decreased and then increased with the increasing Rb doping according to Scanning Electron Microscope (SEM) morphology analysis. Besides that, Raman spectroscopy analyses indicate that the phonon lifetimes of the ZnO-based thin films slightly increased due to the improvement of the crystal quality with the increasing amount of Rb in the SILAR solution. Photosensor measurements of the nanostructured pristine and Rb-doped ZnO thin films were measured at different light power intensities under the visible light environment. Photosensor properties were examined depending on the doping amount and light power density. In light of the literature review, our study is the first to produce Rb-doped ZnO thin films via the SILAR method, which has a promising potential for photosensor applications. Graphical Abstract: (Figure presented.)