Boron-doped strontium-stabilized bismuth cobalt oxide thermoelectric nanocrystalline ceramic powders were produced by using a polymeric precursor technique. The powders were characterized by using x-ray diffraction (XRD), scanning electron microscopy (SEM), and physical properties measurement system (PPMS) techniques. The XRD results showed that these patterns have a two-phase mixture. The phases are face-centered cubic (fcc) and body-centered cubic (bcc). Values of the crystallite size, dislocation density, and microstrain were calculated by using the Scherrer equation. The lattice parameters were calculated for fcc and bcc phases. The SEM results showed that needle-like grains are formed in boron-undoped composite materials, but the needle-like grains changed to the plate-like grains with the addition of boron. The distribution of the nanofiber diameters was calculated and the average diameter of the boron-doped sample is smaller than the boron-undoped one. PPMS values showed that the electrical resistivity values decreased, but the thermal conductivity values, the Seebeck coefficients, and figure of merit (ZT) increased with increasing temperature for the two samples.