Effect of ball-burnishing on surface integrity and fatigue behaviour of 7175-T6 AA


Creative Commons License

Özer M., Dalli K., Özer A.

MATERIALS SCIENCE AND TECHNOLOGY, cilt.39, sa.2, ss.248-257, 2023 (SCI-Expanded)

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 39 Sayı: 2
  • Basım Tarihi: 2023
  • Doi Numarası: 10.1080/02670836.2022.2142744
  • Dergi Adı: MATERIALS SCIENCE AND TECHNOLOGY
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Academic Search Premier, Aerospace Database, Applied Science & Technology Source, Chemical Abstracts Core, Chimica, Communication Abstracts, Compendex, Computer & Applied Sciences, INSPEC, Metadex, Civil Engineering Abstracts
  • Sayfa Sayıları: ss.248-257
  • Gazi Üniversitesi Adresli: Evet

Özet

The burnishing process was performed using different feed rates, rotational speed and penetration depth parameters to alloy Al 7175-T6. Surface roughness, fatigue life and hardness of the samples were determined. Microstructural examinations of the samples were performed. In the surface roughness measurements, occurred a linear increase in proportion to the increasing feed rate. The increase in the penetration depth affected negatively the surface roughness. Significant increases were acquired in the fatigue life of the burnished samples. The hardness values of the burnishing samples are higher than the hardness value of the base material. The rotational movement of the steel ball during the burnishing process were been caused the aspect ratio of the grains in the microstructure to change.