INVESTIGATION OF BENDING STRENGTH OF TANNIN IMPREGNATED WOODEN BEAMS AFTER HEAT TREATMENT

Gunes M., ALTUNOK M.

Wood Research, cilt.68, sa.3, ss.444-454, 2023 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 68 Sayı: 3
  • Basım Tarihi: 2023
  • Doi Numarası: 10.37763/wr.1336-4561/68.3.444454
  • Dergi Adı: Wood Research
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, CAB Abstracts, Compendex, Veterinary Science Database
  • Sayfa Sayıları: ss.444-454
  • Anahtar Kelimeler: acorn tannin, bending strength, Heat treatment, wood modification, wooden beams
  • Gazi Üniversitesi Adresli: Evet

Özet

In this study, the changes in bending strength were investigated by applying heat-treatment to laminated beams modified with acorn tannin to improve the mechanical properties of wooden load-bearing structural members. For this purpose, acorn tannin was impregnated on samples prepared from Scotch pine (Pinus sylvestris L.), oak (Quercus petraea L.), and chestnut (Castanea sativa Mill.) woods. Heat treatment was applied to the samples impregnated with acorn tannin at 150ºC for 3 hours. Untreated, heat-treated, and tannin-modified samples were conditioned until they reached constant weight at 20ºC at 65% relative humidity (RH), 40ºC at 35% RH, and 10ºC at 50% RH. Bending resistance tests were applied to the elements that are conditioned in outdoor conditions according to ISO 13061-3. The results of bilateral interaction between tree species and treatment type were compared, the highest bending strength increase was found in Scotch pine samples by 5% compared to control samples.