Effects of ceramic type, connector dimension, and thermomechanical-aging on the fracture resistance and fit of CAD-CAM produced inlay-retained fixed partial dentures

Güngör M., Nemli S., Inal C. B., Aydin C.

DENTAL MATERIALS JOURNAL, cilt.42, sa.4, ss.523-531, 2023 (SCI-Expanded) identifier identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 42 Sayı: 4
  • Basım Tarihi: 2023
  • Doi Numarası: 10.4012/dmj.2022-230
  • Dergi Adı: DENTAL MATERIALS JOURNAL
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Aerospace Database, Biotechnology Research Abstracts, Communication Abstracts, Compendex, EMBASE, Metadex, Civil Engineering Abstracts
  • Sayfa Sayıları: ss.523-531
  • Anahtar Kelimeler: Adaptation, Aging, CAD-CAM, Ceramics, Fracture resistance
  • Gazi Üniversitesi Adresli: Evet

Özet

The purpose of the present study is to evaluate the fracture resistance and the fit of CAD-CAM produced inlay-retained fixed partial dentures. Eighteen experimental groups were generated according to different CAD-CAM ceramic materials (zirconia, lithium disilicate, and zirconia-reinforced lithium silicate), different connector dimensions (12, 14, and 16 mm(2)), and application of thermomechanical-aging (1,200,000 cycles of cyclic loading with simultaneous thermal cycling). Gap values of thermomechanically-aged groups were measured by using periapical radiographs. Then, the specimens were tested for fracture resistance and failure types were examined. The results were statistically analyzed (alpha=0.05). Higher gap values were observed after aging. Zirconia showed the highest fracture resistance values among the most of the experimental groups. In non-aged groups, the most frequent failure type was decementation in zirconia group. In the aged groups, the most frequent failure type was molar connector fracture. Thermomechanical-aging increased the gap values and decreased the fracture resistance values.