Comparison of the curing kinetic behavior for two epoxy resin systems containing EPIKOTE 828-EPIKURE 3090 and DURATEK KLM 606a-DURATEK KLM 606b


Tuezuen F. N. , Guerue M. , Akyuez Y.

POLYMER COMPOSITES, cilt.28, sa.6, ss.762-770, 2007 (SCI İndekslerine Giren Dergi) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 28 Konu: 6
  • Basım Tarihi: 2007
  • Doi Numarası: 10.1002/pc.20342
  • Dergi Adı: POLYMER COMPOSITES
  • Sayfa Sayıları: ss.762-770

Özet

The aim of the study is to determine the optimum cure temperatures and kinetics for two different epoxy resin systems without using solvent. Two resin systems consist of EPIKOTE 8280 epoxy resin-EPIKURE (R) 3090 poly-amidoamine curing agent and DURATEK (R) KLM 606A epoxy resin-DURATEK (R) KLM 606B polyamide curing agent. The ratio of resin to curing agent was kept as 1:1 for both the systems. Curing temperatures of both the systems were determined and kinetic parameters were calculated with respect to the experimental results following nth-order kinetics. Then, a series of isothermal temperatures was applied to the resin systems in order to assess the cure process in terms of conversion, time, and temperature by using differential scanning calorimeter (DSC). The test results of both systems show that the rate of degree of cure for EPIKOTE 8288 epoxy resin-EPIKURE (R) 3090 poly-amidoamine curing agent system is approximately 10 times higher than that of DURATEK (R) KLM 606A epoxy resin-DURATEK (R) KLM 606B polyamide curing agent system at 230 degrees C.