The effects of some antibacterial nano materials on varnish layer hardness

Creative Commons License

Özder C., Atar M.

JOURNAL OF POLYTECHNIC-POLITEKNIK DERGISI, cilt.26, sa.4, ss.1705-1714, 2023 (ESCI) identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 26 Sayı: 4
  • Basım Tarihi: 2023
  • Doi Numarası: 10.2339/politeknik.1325355
  • Dergi Adı: JOURNAL OF POLYTECHNIC-POLITEKNIK DERGISI
  • Derginin Tarandığı İndeksler: Emerging Sources Citation Index (ESCI), TR DİZİN (ULAKBİM)
  • Sayfa Sayıları: ss.1705-1714
  • Gazi Üniversitesi Adresli: Evet

Özet

The Effects of Some Antibacterial Nano Materials on Varnish Layer Hardness Araştırma Makalesi/Research Article Cansu ÖZDER1* , Musa ATAR2 1Gazi University, Natural and Applied Science Institude, 06500 Ankara, Turkey 2Gazi University, Faculty of Technology, Department of Forestry Industrial Engineering, 06500 Ankara, Turkey (Geliş/Received : 10.07.2023 ; Kabul/Accepted : 10.08.2023 ; Erken Görünüm/Early View : 04.09.2023) ABSTRACT In this study, it was researched the effect of some antibacterial nanomaterial added varnishes on the layer hardness of wood. Samples prepared from Scots pine (Pinus sylvestris L), Oriental beech (Fagus orientalis Lipsky), Sapless oak (Quercus petraea Liebl.) were mixed with 0.1%, 0.3% nano boron (NaB) and nano silver (NaAg), it is varnished with water based and synthetic varnish according to ASTM-D 3023. After varnishing, the surface hardness (oscillation) of the samples was made according to ASTM D 4366-95. As a result; in terms of material type, the highest surface hardness value was determined in Oriental beech, synthetic varnish, nano boron and 0.1% and the lowest in Scotch pine, water based varnish, nano silver and 0.3%. In the multiple interaction, peak Oriental beech+ synthetic varnish+0.1% nano boron (28.00) and least Scotch pine+ synthetic varnish+0.3% nano silver (11.20) were obtained. Compared to the control samples, it was detected nanomaterials had a reducing impact on surface hardness of the varnishes. This may be advantage to consider in application areas where varnish hardness is important. New ideas will emerge with the use of nanomaterials with high antibacterial properties in wood surface treatments and it will provide advantages in usage areas with high risk of abrasion. Key Words: Wood material, hardness, varnish, nano boron, nano silver, modification. Bazı Antibakteriyel Nano Malzemelerin Vernik Katman Sertliğine Etkileri ÖZ Bu çalışmada, bazı antibakteriyel nano malzeme katkılı verniklerin ahşap malzemede katman sertliğine etkisi araştırılmıştır. Sarıçam (Pinus sylvestris L), Doğu kayını (Fagus orientalis Lipsky), sapsız meşeden (Quercus petraea Liebl.) hazırlanan örneklere, %0,1, %0,3 nano bor (NaB) ve nano gümüş (NaAg) ilave edilmiş su bazlı ve sentetik vernik ile ASTM D-3023’e göre verniklenmiştir. Vernikleme işleminden sonra örneklerin yüzey sertliği (salınım) ASTM D 4366-95’e uyularak yapılmıştır. Sonuç olarak; yüzey sertlik değeri malzeme çeşidi bakımından en yüksek, Doğu kayını, sentetik vernik, nano bor ve %0,1’de, en düşük sarıçam, su bazlı vernik, nano gümüş ve %0,3’de tespit edilmiştir. Çoklu etkileşimde en yüksek Doğu kayını+sentetik vernik+%0,1 nano bor (28,00)’de, en düşük sarıçam+sentetik vernik+%0,3 nano gümüş (11,20)’de elde edilmiştir. Kontrol örneklerine göre, nano malzemeler verniklerin yüzey sertliğine azaltıcı etki gösterdiği tespit edilmiştir. Bu durum, vernik sertliğinin önemli olduğu uygulama alanlarında dikkate alınması avantaj sağlayabilir. Antibakteriyel özelliği yüksek olan nano malzemelerin ahşap üst yüzey işlemlerinde kullanılması ile yeni fikirler ortaya çıkacak ve aşınma riski yüksek olan kullanım alanlarında avantaj sağlayacaktır. Anahtar Kelimeler: Ahşap malzeme, sertlik, vernik, nano bor, nano gümüş, modifikasyon