Investigation of Sinterability of WC-Co Component Comprising of AISI 4340 Steel Inserts
GAZI UNIVERSITY JOURNAL OF SCIENCE, cilt.36, sa.4, ss.1722-1731, 2023 (ESCI, Scopus, TRDizin)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 36 Sayı: 4
- Basım Tarihi: 2023
- Doi Numarası: 10.35378/gujs.1070501
- Dergi Adı: GAZI UNIVERSITY JOURNAL OF SCIENCE
- Derginin Tarandığı İndeksler: Emerging Sources Citation Index (ESCI), Scopus, Academic Search Premier, Aerospace Database, Aquatic Science & Fisheries Abstracts (ASFA), Communication Abstracts, Metadex, Civil Engineering Abstracts, TR DİZİN (ULAKBİM)
- Sayfa Sayıları: ss.1722-1731
- Gazi Üniversitesi Adresli: Evet
Özet
In this study, sinterability of WC-9% Co component with AISI 4340 steel insert was investigated using Inserted Powder Injection Molding (IPIM) method. Sintering experiments were performed at temperatures of 1200 degrees C to 1350 degrees C with dwell times of 120, 240, 360 min. Defects such as gaps, cracks and macro-porosities were observed in specimens, sintered at temperatures of 1200 degrees C and 1250 degrees C for all dwell times. It was proved that sintering temperature of 1350 degrees C was as high as it caused insert to get deformed and melted. As a result, the optimum sintering temperature and dwell time were determined to be 1300 degrees C and 240 min, respectively, at which the highest hardness, compression strength, and sintered density were obtained without any defects such as cracks or gaps.