Effect of self and dual-curing on degree of conversion and crosslink density of dual-cure core build-up materials


Karakış D., Yıldırım Biçer A. Z., Doğan A., Koralay H., Çavdar Ş.

JOURNAL OF PROSTHODONTIC RESEARCH, cilt.61, sa.2, ss.210-216, 2017 (SCI-Expanded) identifier identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 61 Sayı: 2
  • Basım Tarihi: 2017
  • Doi Numarası: 10.1016/j.jpor.2016.05.002
  • Dergi Adı: JOURNAL OF PROSTHODONTIC RESEARCH
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED)
  • Sayfa Sayıları: ss.210-216
  • Anahtar Kelimeler: Dual cure resin, Degree of conversion, Glass transition temperature, Self curing, Crosslink density, Hardness, RESIN COMPOSITE, MECHANICAL-PROPERTIES, DENTAL RESINS, BIS-GMA, POLYMERIZATION SHRINKAGE, MONOMER CONVERSION, FILLER MORPHOLOGY, PHOTO-ACTIVATION, KINETIC-ANALYSIS, LUTING CEMENTS
  • Gazi Üniversitesi Adresli: Evet

Özet

Purpose: Dual-cure core build-up resins have been developed to.take advantages of both self and light-cured resin. The aim of present study was to determine the polymerization characteristics of self and dual-cured modes of dual-cure core build-up composites evaluating degree of conversion (DC) and crosslink density by measurement of glass-transition temperature (Tg) and hardness decrease in ethanol.