Lanthanum(III)hydroxide Nanoparticles and Polyethyleneimine-Functionalized Graphene Quantum Dot Nanocomposites in Photosensitive Silicon Heterojunctions


ANTER A., ORHAN E., ULUSOY M., Polat B., YILDIZ M., Kumar A., ...Daha Fazla

ACS Applied Materials and Interfaces, cilt.16, sa.17, ss.22421-22432, 2024 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 16 Sayı: 17
  • Basım Tarihi: 2024
  • Doi Numarası: 10.1021/acsami.4c02102
  • Dergi Adı: ACS Applied Materials and Interfaces
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Chemical Abstracts Core, Compendex, EMBASE, INSPEC, MEDLINE
  • Sayfa Sayıları: ss.22421-22432
  • Anahtar Kelimeler: graphene quantum dots, green method, lanthanum(III) hydroxide doping, nanocomposite diode, photosensitivity, rare earth elements
  • Gazi Üniversitesi Adresli: Evet

Özet

Lanthanides are largely used in optoelectronics as dopants to enhance the physical and optical properties of semiconducting devices. In this study, lanthanum(III)hydroxide nanoparticles (La(OH)3NPs) are used as a dopant of polyethylenimine (PEI)-functionalized nitrogen (N)-doped graphene quantum dots (PEI-NGQDs). The La(OH)3NPs-dopedPEI-NGQDs nanocomposites are prepared from La(NO)3 in a single step by a green novel method and are characterized by Fourier-transform infrared spectroscopy (FT-IR), ultraviolet-visible spectroscopy (UV-vis), X-ray photoelectron spectroscopy (XPS), and transmission electron microscopy (TEM). Deposited over an n-type Si wafer, the La(OH)3NPs-dopedPEI-NGQDs nanocomposites form Schottky diodes. The I-V characteristics and the photoresponse of the diodes are investigated as a function of the illumination intensity in the range 0-110 mW cm-2 and at room temperature. It is found that the rectification ratio and ideality factor of the diode decrease, while the Schottky barrier and series resistance increase with the enhancing illuminations. As a photodetector, the La(OH)3NPs-dopedPEI-NGQDs/n-Si heterojunction exhibits an appreciable responsivity of 3.9 × 10-3 AW-1 under 22 mW cm-2 at −0.3 V bias and a maximum detectivity of 8.7 × 108 Jones under 22 mW cm-2 at −0.5 V. This study introduces the green synthesis and presents the structural, electrical, and optoelectronic properties of La(OH)3NPs-dopedPEI-NGQDs, demonstrating that these nanocomposites can be promising for optoelectronic applications.