Microtensile bond strength and failure type analysis of selfetch adhesive systems on superficial and deep dentin after long-term water storage Análise de resistência de adesão à microtração e tipo de falha de sistemas adesivos autocondicionantes em dentina superficial e profunda após armazenamento longitudinal em água


ÇEVİK P., YILDIRIM A. Z., ARTVİN Z., Özcan M.

Brazilian Dental Science, cilt.23, sa.4, ss.1-12, 2020 (Scopus) identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 23 Sayı: 4
  • Basım Tarihi: 2020
  • Doi Numarası: 10.14295/bds.2020.v23i4.2072
  • Dergi Adı: Brazilian Dental Science
  • Derginin Tarandığı İndeksler: Scopus
  • Sayfa Sayıları: ss.1-12
  • Gazi Üniversitesi Adresli: Evet

Özet

© 2020, Universidade Estadual Paulista, Institute of Science and Technology of Sao Jose dos Campos. All rights reserved.Objective: The aim of this study was to evaluate and compare the microtensile bond strengths of four current adhesive materials that contain different monomers at deep and superficial dentin. Material and Methods: Forty non-carious human third molars (n=5) were used in the study. Specimens were divided into two main groups according to dentin thickness as superficial and deep dentin. Groups were further divided into four subgroups in terms of the adhesive systems used: Nova Compo B Plus (NCBP), Nova Compo B (NCB), Futurabond M (FB) and Clearfil S3 Bond Plus (CS3). All specimens were bonded to resin composite and stored in 37 °C water for 9-months. Teeth were sectioned into 3 x 3 mm thick beams. Microtensile bond strength test was carried out by using a universal testing device (1 mm/min). After fracture, failure types were observed using an optical microscope and the fractured dentin surfaces were observed by a scanning electron microscopy (SEM). One-way ANOVA and Tukey tests were used to compare the adhesive system in each dentin group. An unpaired T-test was used to compare the dentin thickness in each adhesive material. Results: As compared to deep dentin, superficial dentin showed higher µTBS values in groups NCBP, FB and CS, as opposed to group NCB. Only NCB revealed higher bond strength at deep dentin layers when compared to superficial dentin. In the superficial dentin group, NCBP showed the highest bond strength value, while NCB showed the lowest bond strength. In the deep dentin group, while NCB showed the highest bond strength value, NCBP revealed the lowest bond strength value after 9-months storage. While 4-META and 10-MDP monomer combination (NCBP) resulted in the highest bond strength value among the adhesive systems in the superficial dentin group, the GPDMA and 4-META monomer combination (NCB) resulted in the highest bond strength in deep dentin group. Conclusions: Microtensile bond strength performance are affected by both the type of monomer in the adhesive combination and the depth of the dentin.